Percorrer por autor "Yan, Le-Ping"
A mostrar 1 - 4 de 4
Resultados por página
Opções de ordenação
- Bilayered silk/silk-nanoCaP scaffolds for osteochondral tissue engineering: In vitro and in vivo assessment of biological performancePublication . Yan, Le-Ping; Silva-Correia, Joana; Oliveira, Mariana B.; Vilela, Carlos; Pereira, Hélder; Sousa, Rui A.; Mano, João F.; Oliveira, Ana L.; Oliveira, Joaquim M.; Reis, Rui L.Novel porous bilayered scaffolds, fully integrating a silk fibroin (SF) layer and a silk-nano calcium phosphate (silk-nanoCaP) layer for osteochondral defect (OCD) regeneration, were developed. Homogeneous porosity distribution was achieved in the scaffolds, with calcium phosphate phase only retained in the silk-nanoCaP layer. The scaffold presented compressive moduli of 0.4 MPa in the wet state. Rabbit bone marrow mesenchymal stromal cells (RBMSCs) were cultured on the scaffolds, and good adhesion and proliferation were observed. The silk-nanoCaP layer showed a higher alkaline phosphatase level than the silk layer in osteogenic conditions. Subcutaneous implantation in rabbits demonstrated weak inflammation. In a rabbit knee critical size OCD model, the scaffolds firmly integrated into the host tissue. Histological and immunohistochemical analysis showed that collagen II positive cartilage and glycosaminoglycan regeneration presented in the silk layer, and de novo bone ingrowths and vessel formation were observed in the silk-nanoCaP layer. These bilayered scaffolds can therefore be promising candidates for OCD regeneration.
- Combinatory approach for developing silk fibroin-based scaffolds with hierarchical porosity and enhanced performance for cartilage tissue engineering applicationsPublication . Ribeiro, Viviana P.; Yan, Le-Ping; Oliveira, Ana; Oliveira, Joaquim M.; Reis, Rui L.Introduction: The combination of several processing technologies can open the possibility for producing scaffolds with superior performance for tissue engineering (TE) applications. Hydrogels are structurally similar to the natural extracellular matrix microenvironment presenting high elasticity and resistance to compression forces. They have been extensively used in biomedical devices fabrication and for TE applications, including for cartilage defects repair[1]. Recently, it was found that proteins like silk fibroin (SF), presenting tyrosine groups can be used to prepare fast formed hydrogels with controlled gelation properties, via an enzyme-mediated cross-linking reaction using horseradish peroxidase (HRP) and hydrogen peroxide (H2O2)[2],[3]. Moreover, the high versatility, processability and tailored mechanical properties of SF, make this natural polymer attractive for the development of innovative scaffolding strategies for cartilage TE applications[4],[5]. Materials and Methods: The present work proposes a novel route for developing SF-based scaffolds derived from highconcentrated SF (16wt%) enzymatically cross-linked by a HRP/H2O2 complex. The combination of salt-leaching and freeze-drying methodologies was used to prepare macro/microporous SF scaffolds with an interconnected structure and specific features regarding biodegradation and mechanical properties (Fig. 1a). The scaffolds morphology and porosity were analyzed by SEM and micro-CT. The mechanical properties (Instron) and protein conformation (FTIR, XRD) were also assessed. In order to evaluate the scaffolds structural integrity, swelling ratio and degradation profile studies were performed for a period of 30 day. This work also aims to evaluate the in vitro chondrogenic differentiation response by culturing human adipose derived stem cells (hASCs) over 21 days in basal and chondrogenic conditions. Cell behaviour in the presence of the macro/microporous structures will be evaluated through different quantitative (Live/Dead, DNA, GAGs, RT PCR) and qualitative (SEM, histology, immunocytochemistry) assays. Results and Discussion: The macro/microporous SF scaffolds showed high porosity and interconnectivity with the trabecular structures evenly distributed (Fig. 1b,c). A dramatic decrease of compressive modulus was observed for samples in hydrated state. Chemical analysis revealed that SF scaffolds displayed the characteristic peaks for β-sheet conformation. Swelling ratio data demonstrated a large swelling capacity, maintaining their structural integrity for 30 days. As expected, when immersed in protease XIV the degradation rate of SF scaffolds increased. Based on the promising morphology and physicochemical properties of the developed SF scaffolds, in vitro chondrogenic differentiation studies with hASCs are envisioned in order to validate their performance for cartilage regeneration applications.Conclusion: This study proposes an innovative approach to produce fast-formed porous SF scaffolds using enzymatically crosslinked SF hydrogels structured by the combination of salt-leaching and freeze-drying methodologies. The obtained results can provide a valuable reference of SF as a tunable and versatile biomaterial with great potential for applications in cartilage TE scaffolding.
- Combinatory approach for developing silk fibroin-based scaffolds with hierarchical porosity and enhanced performance for cartilage tissue engineering applicationsPublication . Ribeiro, Viviana; Yan, Le-Ping; Oliveira, Ana L.; Oliveira, Joaquim M.; Reis, Rui L.Introduction: The combination of several processing technologies can open the possibility for producing scaffolds with superior performance for tissue engineering (TE) applications. Hydrogels are structurally similar to the natural extracellular matrix microenvironment presenting high elasticity and resistance to compression forces. They have been extensively used in biomedical devices fabrication and for TE applications, including for cartilage defects repair[1]. Recently, it was found that proteins like silk fibroin (SF), presenting tyrosine groups can be used to prepare fast formed hydrogels with controlled gelation properties, via an enzyme-mediated cross-linking reaction using horseradish peroxidase (HRP) and hydrogen peroxide (H2O2)[2],[3]. Moreover, the high versatility, processability and tailored mechanical properties of SF, make this natural polymer attractive for the development of innovative scaffolding strategies for cartilage TE applications[4],[5]. Materials and Methods: The present work proposes a novel route for developing SF-based scaffolds derived from high-concentrated SF (16wt%) enzymatically cross-linked by a HRP/H2O2 complex. The combination of salt-leaching and freeze-drying methodologies was used to prepare macro/microporous SF scaffolds with an interconnected structure and specific features regarding biodegradation and mechanical properties (Fig. 1a). The scaffolds morphology and porosity were analyzed by SEM and micro-CT. The mechanical properties (Instron) and protein conformation (FTIR, XRD) were also assessed. In order to evaluate the scaffolds structural integrity, swelling ratio and degradation profile studies were performed for a period of 30 day. This work also aims to evaluate the in vitro chondrogenic differentiation response by culturing human adipose derived stem cells (hASCs) over 21 days in basal and chondrogenic conditions. Cell behaviour in the presence of the macro/microporous structures will be evaluated through different quantitative (Live/Dead, DNA, GAGs, RT PCR) and qualitative (SEM, histology, immunocytochemistry) assays. Results and Discussion: The macro/microporous SF scaffolds showed high porosity and interconnectivity with the trabecular structures evenly distributed (Fig. 1b,c). A dramatic decrease of compressive modulus was observed for samples in hydrated state. Chemical analysis revealed that SF scaffolds displayed the characteristic peaks for β-sheet conformation. Swelling ratio data demonstrated a large swelling capacity, maintaining their structural integrity for 30 days. As expected, when immersed in protease XIV the degradation rate of SF scaffolds increased. Based on the promising morphology and physicochemical properties of the developed SF scaffolds, in vitro chondrogenic differentiation studies with hASCs are envisioned in order to validate their performance for cartilage regeneration applications.
- Tumor growth suppression induced by biomimetic silk fibroin hydrogelsPublication . Yan, Le-Ping; Silva-Correia, Joana; Ribeiro, Viviana P.; Miranda-Gonçalves, Vera; Correia, Cristina; Morais, Alain da Silva; Sousa, Rui A.; Reis, Rui M.; Oliveira, Ana L.; Oliveira, Joaquim M.; Reis, Rui L.Protein-based hydrogels with distinct conformations which enable encapsulation or differentiation of cells are of great interest in 3D cancer research models. Conformational changes may cause macroscopic shifts in the hydrogels, allowing for its use as biosensors and drug carriers. In depth knowledge on how 3D conformational changes in proteins may affect cell fate and tumor formation is required. Thus, this study reports an enzymatically crosslinked silk fibroin (SF) hydrogel system that can undergo intrinsic conformation changes from random coil to β-sheet conformation. In random coil status, the SF hydrogels are transparent, elastic, and present ionic strength and pH stimuli-responses. The random coil hydrogels become β-sheet conformation after 10 days in vitro incubation and 14 days in vivo subcutaneous implantation in rat. When encapsulated with ATDC-5 cells, the random coil SF hydrogel promotes cell survival up to 7 days, whereas the subsequent β-sheet transition induces cell apoptosis in vitro. HeLa cells are further incorporated in SF hydrogels and the constructs are investigated in vitro and in an in vivo chick chorioallantoic membrane model for tumor formation. In vivo, Angiogenesis and tumor formation are suppressed in SF hydrogels. Therefore, these hydrogels provide new insights for cancer research and uses of biomaterials.