Veiga, AnabelaCastro, FilipaCunha-Reis, CassildaSousa, AurelianaOliveira, AnaRocha, Fernando2020-01-072020-01-072020Veiga, A., Castro, F., Reis, C. C., Sousa, A., Oliveira, A. L., Rocha, F. (2020). Hydroxyapatite/sericin composites: a simple synthesis route under near-physiological conditions of temperature and pH and preliminary study of the effect of sericin on the biomineralization process. Materials Science and Engineering: C, 108, 1104000928-4931http://hdl.handle.net/10400.14/29109Synthesis of hydroxyapatite (HAp) and sericin (SS) nanocomposites was carried out by a simple precipitation method performed in batch in a stirred tank reactor (ST). The reaction was achieved by mixing a solution of calcium chloride dihydrate, in which SS was dissolved, with a solution of disodium hydrogen phosphate at 37 °C. Three experimental conditions were studied by varying the concentration of SS: HAp, HAp/SS1 (0.01 g/L of SS) and HAp/SS2 (1 g/L of SS). The chemical and physical properties of the resulting HAp/SS nanocomposites were studied using several techniques (Atomic Absorption Spectrometry, Ultraviolet-Visible Spectrophotometry, Fourier Transform Infrared Spectroscopy (FTIR), X-ray diffraction (XRD), Scanning electron microscopy (SEM), Transmission electron microscopy (TEM), Selected area diffraction (SAED) and Thermogravimetric analysis (TGA)). pH profile was also monitored over time for each experimental condition. The results revealed that nano single-phased HAp was formed with both rod and plate-like shape. Additionally, the particles have low crystallinity, characteristic similar to biological HAp. Regarding the influence of SS, one observed that with increasing SS concentration there is an increase in the mean particle size and the number of plate-like particles, as well as an increase in the aggregation degree and a decrease of the crystallinity. Further, the composites obtained have an inorganic/organic composition comparable to bone. Finally, in vitro cytotoxicity showed that the synthetized nanoparticles are non-toxic and cell viability is higher for HAp and HAp/SS samples when compared to a commercially available HAp. The produced materials can thus be considered suitable candidates for bone related applications.engHydroxyapatite (HAp)Sericin (SS)NanocompositesPrecipitationStirred tank (ST)journal article10.1016/j.msec.2019.1104008507519866531923995000510956400048